14years production experience
We have been focusing on the production of various grips, mark tube and insulating tube for 14 years, such as handle tool grips, stick grips, etc.,We customize various protection solutions for custome14years production experience
We have been focusing on the production of various grips, mark tube and insulating tube for 14 years, such as handle tool grips, stick grips, etc.,We customize various protection solutions for custome
Technical Data
| Property | Test Method | Standard Value |
| Tensile Strength | ASTM-D-638 | ≥12MPa |
| Elongation at Break | ASTM-D-638 | ≥300% |
|
Tensile Strength Variation After Heat Aging（130℃x168h） |
ASTM-D-5510 | ≤±20% |
|
Elongation at Break Variation After Heat Aging（130℃x168h） |
ASTM-D-5510 | ≤±20% |
| Dielectric Strength | IEC 60243 | ≥15kV/mm |
| Volume Resistivity | IEC 60093 | ≥1x1013Ω.cm |
| Brittle Temperature | ISO 974 | -40℃ |
| Heat Shock | 160℃，4h | No Crack |
| Water Absorption | ISO 62 | ≤0.1% |
| Hardness（Shore A） | ISO 868 | ≥80 |
| Longitudinal Shrinkage | ASTM-D-2671 | ≤10% |
| Eccentricity | ASTM-D-2671 | ≤30% |
| Spec. | As Supplied/mm | After Recovered/mm | Standard Length /mm | ||
| Width(W) Min |
Thicknes (T=±0.3mm) |
Width(W) Max |
Thickness
(T=±0.3mm)
|
||
| WRSXP-30/12 | 120 | 1.3 | 38 | 3.8 | 450-1200 |
| WRSXP-40/12 | 130 | 1.2 | 38 | 3.8 | 450-1200 |
| WRSXP-50/17 | 160 | 1.3 | 53 | 3.8 | 450-1200 |
| WRSXP-65/24 | 205 | 1.2 | 75 | 3.8 | 450-1200 |
| WRSXP-85/27 | 270 | 1.3 | 82 | 3.8 | 450-1200 |
| WRSXP-100/27 | 320 | 1.4 | 82 | 3.8 | 450-1200 |
| WRSXP-120/40 | 380 | 1.4 | 129 | 3.8 | 450-1000 |
| WRSXP-150/50 | 475 | 1.4 | 157 | 3.8 | 450-1000 |
| WRSXP-160/50 | 505 | 1.3 | 157 | 3.8 | 450-1000 |
| WRSXP-170/51 | 535 | 1.2 | 160 | 3.8 | 450-1000 |
| WRSXP-180/51 | 565 | 1.1 | 160 | 3.8 | 450-1000 |
| WRSXP-195/52 | 590 | 1 | 163 | 3.8 | 450-1000 |